Principal Applications

  • Condensate Polishing


  • Excellent physical and chemical stability
  • High breaking weight
  • High linear velocity applications
  • High operating capacity
  • Lower pressure drop versus standard resin
  • Superior osmotic shock resistance


  • Condensate polishing mixed beds
  • Condensate polishing lead cation
  • High Temperature

Typical Packaging

  • 1 ft³ Sack
  • 25 L Sack
  • 5 ft³ Drum (Fiber)
  • 1 m³ Supersack
  • 42 ft³ Supersack

Typical Physical & Chemical Characteristics:

Polymer Structure Gel polystyrene crosslinked with divinylbenzene
Appearance Spherical Beads
Functional Group Sulfonic Acid
Ionic Form H+ form
Total Capacity 2 eq/L (43.7 Kgr/ft³) (H+ form)
Moisture Retention 46 - 50 % (H+ form)
Mean Diameter 650 ± 50 µm
Uniformity Coefficient 1.1 - 1.2
Reversible Swelling, Na+ → H+ (max.) 8 %
Specific Gravity 1.21
Shipping Weight (approx.) 770 - 790 g/L (48.1 - 49.4 lb/ft³)
Temperature Limit 120 °C (248.0 °F)

Hydraulic Characteristics

Pressure Drop

The pressure drop across a bed of ion exchange resin depends on the particle size distribution, bed depth, and voids volume of the exchange material, as well as on the flow rate and viscosity of the influent solution. Factors affecting any of these parameters— such as the presence of particulate matter filtered out by the bed, abnormal compressibility of the resin, or the incomplete classification of the bed—will have an adverse effect, and result in an increased head loss. Depending on the quality of the influent water, the application and the design of the plant, service flow rates may vary from 10 to 40 BV/h.

Pressure Drop Across Resin Bed


During up-flow backwash, the resin bed should be expanded in volume between 50 and 70% for at least 10 to 15 minutes. This operation will free particulate matter, clear the bed of bubbles and voids, and reclassify the resin particles ensuring minimum resistance to flow. When first putting into service, approximately 30 minutes of expansion is usually sufficient to properly classify the bed. It is important to note that bed expansion increases with flow rate and decreases with influent fluid temperature. Caution must be taken to avoid loss of resin through the top of the vessel by over expansion of the bed.

Backwash Expansion of Resin Bed