Chromalite CGA200x8Ac is a chromatographic anion exchange resin with a polymer designed for small organic and inorganic compound separation and purification. It contains 200 μm styrenic resin beads crosslinked with 8% divinylbenzene (DVB). Our proprietary manufacturing method creates perfectly spherical beads with exceptional kinetic and packing properties.

Unlike similar products on the market, Chromalite CGA and CGC resins are supplied in highly pure form (very low extractables content) and do not require pre-treatment. As such they are suitable for pharmaceutical applications.

Supplied in Acetate form.

Equivalent to:
- Dowex® 1X8 50-100 mesh (Dow)
- AG 1-X8 Resin (Bio-Rad)

Note: 

CGA resins occasionally exhibit an amine odour after prolonged storage (this will not affect performance).

In such cases it is recommended to rinse the affected resin with sufficient volumes of water to remove the odour before putting the resin into service.

Principali applicazioni

  • Peptide salt exchange from trifluoroacetate to acetate form in SPPS
  • Cromatografia a scambio ionico
  • Dissalazione delle biomolecole dopo fermentazione
  • Idoneo per la separazione di molecole inorganiche, organiche e biologiche

Vantaggi

  • Alta stabilità chimica
  • Alta capacità
  • Granulometria grossa ottima per impaccamento di grandi colonne
  • Resine cromatografiche altamente purificate
  • Eccezionali proprietà cinetiche e di impaccamento per separazioni cromatografiche

Certificazioni

  • Conforme al regolamento FDA 21 CFR 173.25
  • Compliant with ResAP(2004) 3
  • Halal
  • Kosher
  • esente da TSE BSE OGM

Imballi tipici

  • 250 g
  • 1 kg

Caratteristiche chimiche e fisiche tipiche:

Aspetto Pale yellow to dark yellow spherical beads
Gruppo funzionale Quaternary Ammonium
Fornito come Acetate form (Ac conversion >85%) in 20% EtOH solution
Capacità volume (min.) 1.2 eq/L
Capacità peso (min.) 3.5 eq/kg
Distribuzione granulometrica (90% nel range) 150 - 300 µm
Distribuzione granulometrica (90% nel range) 50 - 100 mesh
Diametro Medio 200 - 250 µm
Coefficiente di uniformità (max.) < 1.5
Umidità totale 45 - 60 percento
Limite di stabilità del pH 1 - 14
Condizioni ottimali di conservazione 2 - 20 °C
Data di scadenza (dalla data di produzione) 5 anni
% Crosslinking 8